Surface area and porosity

  1. Haber, Jerzy comp.
  2. M. del Arco col.
Revista:
Catalysis Today

ISSN: 0920-5861

Año de publicación: 1994

Volumen: 20

Número: 1

Páginas: 11-16

Tipo: Artículo

DOI: 10.1016/0920-5861(94)85010-0 GOOGLE SCHOLAR lock_openAcceso abierto editor

Otras publicaciones en: Catalysis Today

Resumen

The BET surface area was found to be 10.5 (±0.5), 10.1 (±0.5) and 11.0 (±0.5) m2 g−1 for sample EL10, EL10V1 and EL10V8, respectively. No microporosity was observed for any of the samples. In all cases, a bimodal distribution of porosity was observed, indicating intraparticle macroporosity with radii about 0.1–0.2 and interparticle porosity radii around 10 μm. The TiO2 support is composed of particles with radii of about 1 μm, these forming aggregates of loosely coherent particles (radii ⋍ 100 μm). Impregnation by the V2O5 compound does not modify appreciably either the surface area or the degree of aggregation